How to improve the service life of vacuum induction furnace lining

How to improve the service life of vacuum induction furnace lining
Induction of the vacuum furnace lining refractory materials used for the high temperature performance mainly depends on the physical and chemical properties and mineral composition, on the premise of raw and auxiliary materials selection, sintering process is to make the lining have good microscopic structure to give full play to its high temperature resistant performance of the key working procedure. Lining sintering densification degree and refractory material ratio of the chemical composition, particle size, sintering process and sintering temperature and other factors. Ningbo shekinah electric co., LTD., through ten years of trial and error and production test, summarized the knot reasonable construction technology and baking sintering process, the sharp rise in the furnace life, induction furnace life of vacuum furnace dry rammed lining (a long) as much as 1157 times, has obtained the remarkable economic benefits.
Second, the construction process
1, when the furnace building remove mica paper.
2, the furnace building made of crystal quartz sand as follows:
Hand picking, mainly eliminate block and other impurities;
Magnetic separation: the magnetic must be completely removed;
Dry ramming material: must slow drying processing, baking temperature of 200 ℃ to 300 ℃, heat preservation more than 4 hours.
3, the selection of binder: with boron anhydride (B2O3) instead of boric acid (H3BO3) as a binder, the addition amount of 1.1% to 1.1%.